slag inclusion
英 [slæɡ ɪnˈkluːʒn]
美 [slæɡ ɪnˈkluːʒn]
网络 夹渣; 夾渣
双语例句
- Reaction of rare earth with oxygen and sulfur can improve the shape of slag inclusion while purifying surfacing.
稀土钇与氧、硫结合在净化堆敷金属的同时，改善了堆敷金属中夹渣物的形态。 - By using this process to repair castings, there is no obvious separating line, no slag inclusion and gas hole between the welding zone and base metal.
用此工艺焊补铸件，焊补区域与基体间没有明显的熔合线，无渣孔、气孔等缺陷。 - This article analyzes the weld defects such as: blowhole, slag inclusion, incompletely filled groove, overlap, lack of fusion, undercut, over-sized leg, also it puts forward the solution.
对立角焊中气孔、夹渣、未焊透、焊缝余高凸起、焊波脱节、咬边、焊脚尺寸过大等缺陷产生的原因进行了分析，并提出了有效的解决方法。 - The reasons causing sand inclusion and slag inclusion are: ( 1) gaps between mould and core prints or cods too small;
前言：湿砂型铸铁件产生砂孔和渣孔缺陷的主要原因是：（1）芯头或砂台的间隙偏小； - Utilizes the balanced coagulation technology solution plate class casting the entrapped slag, the sand inclusion, flaws and so on blowhole, improves the casting quality, reduces rejection rate.
运用均衡凝固技术解决平板类铸件的夹渣，夹砂和气孔等缺陷，提高铸件质量，降低废品率。 - The linear is slag inclusion on the sides of weld joints.
焊缝两侧的不规则线条一般为夹渣； - The result shows that slag inclusion in continuous casting billet cause the infolding, and the way to reduce infolding by improving the quality of billet is suggested.
结果表明，连铸坯中心存在大量夹渣物，致使在穿孔轧制过程中形成内折缺陷。提出了改进措施。 - When% Al2O3/% CaO is more than 0.9, that adsorption of Al2O3 in refining slag would be improved with decreasing of original Al2O3 content, enhancing of saturated concentration of Al2O3, decreasing of viscosity of slag and interface tension between slag and Al2O3 inclusion.
重庆大学硕士学位论文当A12o3/cao二0.9一1.2时，降低熔渣粘度和减少渣中初始A1203含量，以及减少熔渣与A1203夹杂之间的界面张力均有利于改善熔渣吸收A1203夹杂的能力。 - There are seventy-six eligible castings to be produced by using the technology without shrinkage, porosity shrinkage, blowhole and slag inclusion after machining.
用此工艺连续生产76件，总重230t，铸件加工后，没有缩孔、缩松、气孔、渣孔缺陷，全部合格。 - Answers to Some Molding Sand-Related Questions in Green Sand Mold Iron Castings Production(ⅲ)& Questions related with blowhole, sand and slag inclusion defects
湿型铸铁件生产中一些与型砂有关的问题解答（三）&与气孔、砂孔、渣孔缺陷有关的问题 - Reason and Prevention of Top-surface Slag Inclusion on Cooling Wall of Nodular Iron Casting
球铁冷却壁上表面夹渣的原因及防止 - The bedded crack on low plain longitudinal node plate is caused by rejected steel quality and slag inclusion in interlayer while smelting.
下平纵联节点板呈现的层状撕裂是由于材质不合格及冶炼时层间夹碴引起的。 - The slag inclusion in the slab shell formed in casting mould was analyzed by applying Color-CCD-Video Microscope.
本文采用彩色视频显微仪对连铸结晶器内铸坯的卷渣情况进行研究。 - Laboratory Research on Effect of Slag Dam in Tundish on Inclusion Floating
中间罐挡渣装置对夹杂物上浮影响的实验研究 - To study the effect of slag dam in tundish on inclusion floating, laboratory test has been done.
为了研究中间罐挡渣装置对夹杂物上浮的影响，进行了实验室研究。 - The artificial neural network designed and trained gave the percentage of crack growing, slag inclusion cracking, residual stress releasing and structure rubbing signals for a complex AE source.
设计和培训的人工神经网络可以给出一个多种因素产生的复合声发射源中裂纹扩展、氧化夹渣断裂、残余应力释放和机械摩擦信号所占的百分比。 - In the production process of tire cord steel, total oxygen and inclusion composition is controlled by using Si-Mn alloy and changing refining slag. The inclusion morphology is improved greatly.
在帘线钢的生产中，通过采用Si-Mn合金终脱氧以及改变精炼渣系，达到控制钢中酸溶铝含量，进而控制钢中夹杂物组成的目的，改善了夹杂物形态； - Formation mechanism and characters of major defects on stainless steel billet such as depression, crack, slag inclusion and deep oscillation mark, not easy to be removed, are analyzed considering steel composition, solidification character, thermal and mechanical properties.
从不锈钢的组成、凝固特点以及高温热性能和力学性能等方面具体分析不锈钢铸坯表面凹陷、裂纹、夹渣以及不易除掉的深振痕等缺陷产生的机理和特征。 - A Study on Dynamics of Al_2O_3-CaO Base Pre-molten Refining Slag to Absorb Al_2O_3 Inclusion
Al2O3-CaO基预熔精炼渣吸收Al2O3夹杂的动力学研究 - The effect of top slag composition on MnO-Al2O3-SiO2 inclusion composition was studied by controlling the condition of deoxidization and the composition of top slag in an experimental furnace in which the tire cord steel were melt.
在实验室中使用高温管式炉对以工业纯铁为原料配制的帘线钢进行脱氧和顶渣熔炼，研究了顶渣成分对MnO-Al2O3-SiO2类夹杂物的成分的影响。 - The common defects of the housing casting include cracks, sand drop, slag inclusion, shrinkage porosity and rough grain, etc.
机架的常见缺陷有裂纹、掉砂、夹渣、缩孔缩松和晶粒粗大等。 - Inclusion content, especially large oxide inclusion is high in small converter because of nonstandard in slag stopping and argon bubbling stirring, short of floating time of inclusion, bad protecting of teeming system. The large foreign inclusions are bad to steel properties.
小转炉由于出钢挡渣、钢水吹氩搅拌不规范、钢中夹杂物上浮时间不足、浇钢系统保护不好，造成钢中夹杂物含量高，特别是大型氧化物夹杂数量多； - Influence of Basicity of Slag to Inclusion of Ball Bearing Steel
炉渣碱度对轴承钢夹杂物的影响 - Analysis of the Influence of Slag Inclusion in Steel Plate on the Quality of Electric Resistance Welding Pipeline
钢板中夹杂物对高频电阻焊管质量影响浅析 - The results showed that the oxidation slag inclusion and central porosity in the raw material were the direct reasons which the forging cracking.
结果表明，锻坯原材料中存在的中心疏松和氧化物夹渣等低倍缺陷是导致锻件开裂的主要原因。 - When fabricating nodular cast iron piston rings, subcutaneous blowholes, shrinkage porosity, slag inclusion and reverted chill often happen due to the paste solidification characteristics, which are so bad to the mechanical property of nodular piston ring.
由于球墨铸铁的糊状凝固特性，在球墨铸铁活塞环的生产中，极易产生皮下气孔、缩松、夹渣及反白口等主要铸造缺陷，使得球铁环的力学性能受到极大的影响。 - Magnesium alloy is the preferred material for manufacture of lightweight structures thanks of a series of extraordinary features. However, the fusion welding method results easily defects like cracks, slag inclusion, splashing and bigger deformation.
镁合金是结构轻量化的首选材料，在焊接方面，采用传统的弧焊方法很容易产生裂纹、夹渣、飞溅和大变形等缺陷。 - In the practical application of the equipment, fracture splitting defects such as drop clinker and slag inclusion can be reduced and the laser cutting parameters and hardness of lower limit can be improved.
裂解槽激光加工自动化设备在实际应用中，能够减少爆口、夹渣等裂解缺陷，并可以通过改变激光切割参数，改善硬度处于裂解工艺要求下限的连杆的裂解质量。 - And then, with the increase of basicity in refining slag, the range of Al2O3 content in inclusion increases with the content of Al2O3 in refining slag is larger.
而且随精炼渣碱度的增加，夹杂物A1203含量随精炼渣A1203含量增加而增加的幅度变大。